EVALUATION OF THE MASTER CURVE APPROACH FOR THE NON-ISOTHERMAL CRYSTALLIZATION OF PP/EPR

Autores/as

  • Alessandra Lucas Marinelli
  • Benjamim de Melo Carvalho
  • Rosario Elida Suman Bretas

DOI:

https://doi.org/10.5212/publicatio.v10i03.833

Resumen

The purpose of the present work was to test the validity of the Master Curve Approach in order to determine the nonisothermal crystallization constant for a heterophasic polypropylene (PP/EPR). Nonisothermal crystallization experiments were carried out in a DSC at several cooling rates, and the original curves were corrected because of the temperature lag between the samples and the furnace. Through the use of the nonisothermal kynetic crystallization constant, determined by the Master Curve Approach, and the use of the Nakamura equation, the curves of relative cristallinity in relation to temperature were simulated and compared with the corresponding curves obtained from experimental data. A relatively good agreement with the experimental curves was obtained.

Key words: ethylene-propylene rubber, crystallization, master curve approach, heterophasic polypropylene

Descargas

Publicado

2009-12-03

Número

Vol. 10 Núm. 03 (2004)

Sección

Artigos

Licencia

As propostas, originais e inéditas, redigidas em português ou em inglês, preferencialmente, não podem simultaneamente serem submetidas a outros periódicos, e devem ser acompanhadas de uma autorização formal para publicação emitida pelo autor princA Revista, com periodicidade quadrimestral e editada de forma eletrônica, não cobra qualquer tipo de despesa e nem faz qualquer tipo de pagamento ou ressarcimento aos autores. Embora a Revista reserve todos os direitos autorais do trabalho publicado permitindo a sua reprodução, com citação da fonte, o conteúdo das publicações continua de inteira responsabilidade dos autores, não refletindo a opinião dos Editores. ipal.